Зміна механічних та електрохімічних характеристик сталі газопроводів після тривалої експлуатації
Keywords:
metal properties degradation, microcrack, metal inundation.Abstract
Degradation of the gas trunk pipelines’ material characteristics due to the ageing process can occur during long-term operation. The investigations of the trunk pipeline characteristics which have been in operation 35-40 years showed that long-term pipeline operation causes neglectable degradation of the normed mechanical and
electro-chemical properties of the low-alloyed tubular steals. The degradation can not cause a serious danger if the propriate control of the pipe wall thickness will be organized.
Downloads
Download data is not yet available.
References
1 Covino B.S. Detecting internal corrosion of natural gas transmission pipelines: Field tests of probes and systems for real-time corrosion measurement / B.S.Covino, Jr. S.J.Bullard, S.D.Cramer, et al. // Proceedings of the European Corrosion Congress “Eurocorr2005”, Lisbon, 2005. – Paper #396.
2 Graves J.W. Internal corrosion in gas gathering systems and transmission lines / Graves J.W., Sullivan E.H. // Mater. Prot. – 1996. #5. – Pp. 33- 37.
3 Gabeta G. In-service degradation of gas trunk pipeline X52 / G.Gabeta, H.V.Nykyfor-chyn, E.Lunarska et al. // Фіз.-хім. механіка матеріалів. – 2008. – № 1. – С.88 – 99.
4 Nesic S. Key issues related to modeling of internal corrosion of oil and gas pipelines. A review. Review / Nesic S. // Corrosion Science. Vol.49, Issue 12, 2007. – Pp. 4308 – 4338.
5 Nyborg R. Top of line corrosion and water condensation rates in wet gas pipelines /
Nyborg R., Dugstad A. // Conference and Expo Corrosion 2007. – Paper # 07555. – Houston,
TX: NACE, 2007. – 10 p.
6 Крижанівський Є.І. Вплив наводнення на корозійно-механічні властивості зварних швів газопроводів / Крижанівський Є.І., Тараєвський О.С., Петрина Д.Ю. // Розвідка та розробка нафтових і газових родовищ. – 2005. – № 1 (14). – С.25–29.
7 Иванцов О.М. Надежность магистраль-ных трубопроводов / Иванцов О.М., Харито-нов В.И. – М.: Недра, 1978. – 166 с.
8 Корозія металів і сплавів. Терміни та визначення основних понять : ДСТУ 3830-98. – К.: Держстандарт України, 1999. – 31 с.
9 Похмурський В.І. Вплив вод¬ню на дифузійні процеси в мета¬лах / Похмурський В.І.,
Федоров В.В. – Львів: ФМІ НАН України, 1998. – 206 с.
10 Оцінювання роботоздатності сталі 17Г1С після тривалої експлуатації на газогоні / О.Т.Цирульник, М.І.Греділь, О.З.Студент,
Г.М.Никифорчин // Вісник Тернопільського державного університету. – 2008. – Т.13. – № 4. – С. 49–55.
11 Вплив експлуатації сталі Х52 на коро-зійні процеси у модельному розчині ґазового конденсату / О.Т.Цирульник, З.В.Слободян, О.І.Звірко, М.І.Греділь, Г.М. Никифорчин,
Д. Габетта // Фіз.-хім. механіка матеріалів. – 2008. – Т.44. – №5. – С.29-37.
2 Graves J.W. Internal corrosion in gas gathering systems and transmission lines / Graves J.W., Sullivan E.H. // Mater. Prot. – 1996. #5. – Pp. 33- 37.
3 Gabeta G. In-service degradation of gas trunk pipeline X52 / G.Gabeta, H.V.Nykyfor-chyn, E.Lunarska et al. // Фіз.-хім. механіка матеріалів. – 2008. – № 1. – С.88 – 99.
4 Nesic S. Key issues related to modeling of internal corrosion of oil and gas pipelines. A review. Review / Nesic S. // Corrosion Science. Vol.49, Issue 12, 2007. – Pp. 4308 – 4338.
5 Nyborg R. Top of line corrosion and water condensation rates in wet gas pipelines /
Nyborg R., Dugstad A. // Conference and Expo Corrosion 2007. – Paper # 07555. – Houston,
TX: NACE, 2007. – 10 p.
6 Крижанівський Є.І. Вплив наводнення на корозійно-механічні властивості зварних швів газопроводів / Крижанівський Є.І., Тараєвський О.С., Петрина Д.Ю. // Розвідка та розробка нафтових і газових родовищ. – 2005. – № 1 (14). – С.25–29.
7 Иванцов О.М. Надежность магистраль-ных трубопроводов / Иванцов О.М., Харито-нов В.И. – М.: Недра, 1978. – 166 с.
8 Корозія металів і сплавів. Терміни та визначення основних понять : ДСТУ 3830-98. – К.: Держстандарт України, 1999. – 31 с.
9 Похмурський В.І. Вплив вод¬ню на дифузійні процеси в мета¬лах / Похмурський В.І.,
Федоров В.В. – Львів: ФМІ НАН України, 1998. – 206 с.
10 Оцінювання роботоздатності сталі 17Г1С після тривалої експлуатації на газогоні / О.Т.Цирульник, М.І.Греділь, О.З.Студент,
Г.М.Никифорчин // Вісник Тернопільського державного університету. – 2008. – Т.13. – № 4. – С. 49–55.
11 Вплив експлуатації сталі Х52 на коро-зійні процеси у модельному розчині ґазового конденсату / О.Т.Цирульник, З.В.Слободян, О.І.Звірко, М.І.Греділь, Г.М. Никифорчин,
Д. Габетта // Фіз.-хім. механіка матеріалів. – 2008. – Т.44. – №5. – С.29-37.
Downloads
Published
2009-06-23
How to Cite
Похмурський D. S., & Крижанівський, Є. І. (2009). Зміна механічних та електрохімічних характеристик сталі газопроводів після тривалої експлуатації. Scientific Bulletin of Ivano-Frankivsk National Technical University of Oil and Gas, (3(21), 5–10. Retrieved from https://nv.nung.edu.ua/index.php/nv/article/view/294
Issue
Section
ТRANSPORT AND STORAGE OF OIL AND GAS
License
Авторські права....
1.png)
1.png){kind=logo}